Highly functional and reactive adhesives (Aron Mighty series)
|
|
|
|
|
The Aron Mighty series is composed of highly functional and reactive adhesives. Distinct grades are available including epoxy, urethane, nylon, and acrylic systems which were developed using Toagosei's unique technology. These adhesives are used in diverse fields such as electronic materials, automobiles, and residential building materials.
|
|
Epoxy system adhesives
|
Aron Mighty AP and AS series
|
|
|
Characteristics of the Aron Mighty AP and AS series
|
| Aron Mighty AP series |
Solvent-free type epoxy adhesives. Various cure types are available. Selection can be made according to application and adhesion method. |
|
| Aron Mighty AS series: |
Solvent type epoxy adhesives. Suitable for film lamination |
| Types |
One-liquid, heat cure type |
Two-liquid type, cured at normal temperature |
Solution type |
Primer |
| Grades |
AP-0786 * |
AP-400BD
A agent* |
AP-400BD
B agent* |
AS-60 |
AS-315 * |
S-10 |
| Appearance |
Pale yellow |
Blue |
Opaque white |
Transparent, pale yellow |
Transparent, pale yellow |
Transparent, yellow |
Viscosity
(mPa/s,25ºC) |
11,000 |
35,000 |
35,000 |
500 |
1,300 |
50 |
| Solid content(%) |
100 |
100 |
22 |
30 |
10 |
| Standard curing conditions |
70ºC×60min |
Normal temperature×1day(60min)*1 |
150ºC×30min |
160ºC×60min |
180ºC×10min |
| Characteristics |
Low temperature cure
Strength when cold cured |
Superior flexibility and peeling strength
Mixing ratio (weight) = 1:1 |
Flexible, good adhesion to polyimide, high heat resistance |
Non-halothane type, high heat resistance, short curing time |
Adhesion to metallic materials, increased adhesion, low viscosity |
| Applications |
Fixation of optical pickup components |
Adhesion of building material panels |
FPC, polyimide laminates |
Primer |
|
|
Urethane system adhesives
|
Aron Mighty PU series
|
|
|
Characteristics of Aron Mighty PU series
|
Aron Mighty PU series is composed of urethane adhesives which strongly adhere to various plastics and metals.
Urethane resins are used as raw materials, and flexible and strong cured products are produced. These cured products have both durability and flexibility and used in applications such as automobile parts.
| Types |
Two-liquid system, heat cured |
Two-liquid system, cured at normal temperature |
| Grades |
PU-62 A agent |
PU-62 B agent |
PU-9000 |
PU-171 |
| Appearance |
Gray |
White |
Pale yellow |
| Viscosity(mPa/s,25ºC) |
110,000 |
30,000 |
1,000 |
1,500 |
| Solid content(%) |
100 |
15 |
75 |
| Solvent |
- |
MEK/methyl acetate |
| Standard curing conditions |
Mixing ratio(weight ratio)=10:825ºC×3days,80ºC×30min |
Mixing ratio(weight ratio)=10:125ºC×5hours,90ºC×2min |
| Applications |
Automobile parts
Sealant |
Exteriors of automobiles |
|
|
Nylon system adhesives
|
Aron Mighty FS series
|
|
|
Characteristics of Aron Mighty FS series
|
Aron Mighty FS series is composed of adhesives containing thermoplastic nylon modified to have heat curability. Due to its unique design, this adhesive has retained the elasticity of rubber. It also has a good balance of tensile shear strength and peeling strength. It can be used as a primer for one-piece injection-extrusion molding.
| Types |
One-liquid, heat cured system |
| Grades |
FS-175SV10 |
| Appearance |
Opaque white |
| Viscosity(mPa/s,25ºC) |
60 |
| Solid content (%) |
10 |
| Solvent |
Denatured alcohol |
| Standard curing conditions |
120ºC×3min |
| Applications |
Adhesion for automobile molds |
|